POP/081S/SK Global Chemical 物性表
POP/081S/SK Global Chemical
规格用途
| 该料用途 | 包装; 食品包装 |
| 备注说明 | Supreme™ 081S, Polyolefin Plastomer (POP), is an ethylene-octene copolymer produced via Nexlene™ technology. Supreme™ 081S performs well in a wide range of various food & non-food packaging films with excellent sealing property and impact strength.Typical Performance: Compiles with: Additives: |
技术参数
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 薄膜 | 薄膜厚度 - 经测试 | ASTM D374 | | µm | 割线模量 | ASTM D882 | 1% 正割, MD : 40 µm | 쐡쐡. | MPa | 1% 正割, TD : 40 µm | 뜶 | MPa | 抗张强度 | ASTM D882 | MD : 断裂, 40 µm | 뜡.뜶 | MPa | TD : 断裂, 40 µm | .뜶 | MPa | 伸长率 | ASTM D882 | MD : 断裂, 40 µm | | % | TD : 断裂, 40 µm | 덴 | % | 落锤冲击 | ASTM D1709A | 40 µm | > 뜶 | g | 埃尔曼多夫抗撕强度 | ASTM D1922 | MD : 40 µm | 뜶덴 | g | TD : 40 µm | 덴 | g |
| 物理性能 | 密度 / 比重 | ASTM D792 | .쐡쐡 | g/cm³ | 熔流率（熔体流动速率） | ASTM D1238 | 190°C/2.16 kg | . | g/10 min |
| 挤出 | 熔体温度 | 뜶 到 뜶 | °C | ||
| 光学性能 | 雾度 | ASTM D1003 | 뜡. | % | Sealing Initial Temperature | 内部方法 | 쐡 | °C |
| 热性能 | 维卡软化温度 | ASTM D1525 | 쐡. | °C | 熔融温度 | 内部方法 | 뜶 | °C |