基本参数

艾博（国际）塑胶进出口有限公司现货供应 ExxonMobil LD 302.56 High Clarity，原产原包，可随货提供原材料物性，COA,SGS.MSDS.UL黄卡等相关详细资料，欢迎来人来电咨讯

ExxonMobil LD 302.56 High Clarity

LD 302系列膜具有优异的冲击强度，良好的热封性，良好的低温性能。典型的应用是冷冻食品包装或其他食品包装

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in3	ExxonMobil Method
Vinyl Acetate Content	3.5 %	3.5 %	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	1.3 g/10 min	1.3 g/10 min	ExxonMobil Method
Antiblock Level	3000 ppm	3000 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	8.27 MPa	1200 psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	8.14 MPa	1180 psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	580 %	580 %	ASTM D882
Film Elongation at Yield, MD	6.7 %	6.7 %	ASTM D882
Film Elongation at Yield, TD	5.7 %	5.7 %	ASTM D882
Elmendorf Tear Strength MD	190 g	190 g	ASTM D1922
Elmendorf Tear Strength TD	110 g	110 g	ASTM D1922
Elmendorf Tear Strength, MD	4.984 g/micron	126.6 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	2.89 g/micron	73.3 g/mil	ASTM D1922
Dart Drop	4.461 g/micron	113.3 g/mil	ASTM D1709
Dart Drop Test	170 g	0.375 lb	ASTM D1709
Film Tensile Strength at Break, MD	24.2 MPa	3510 psi	ASTM D882
Film Tensile Strength at Break, TD	23.2 MPa	3370 psi	ASTM D882
1% Secant Modulus, MD	146 MPa	21200 psi	ASTM D882
1% Secant Modulus, TD	172 MPa	24900 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	105 °C	221 °F	Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature	92.0 °C	198 °F	ExxonMobil Method
Vicat Softening Point	88.3 °C	191 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	6.5 %	6.5 %	ASTM D1003
Gloss	69 %	69 %	45°; ASTM D2457
Transmission, Visible	90 %	90 %	clear; thickness not quantified