Ashley Polymers Ashlene® 79MGS Nylon 6, 40% Glass Mineral reinforced

Polymer,Thermoplastic,Nylon,Nylon 6,Nylon 6, Glass/Mineral Reinforced

Ashley Polymers

产品说明:

A 40% glass mineral reinforced Nylon 6 with good dimensional stability, stiffness, sink and warp resistance. Modified for improved surface appearance.

Data provided by the manufacturer

Ashley Polymers Ashlene® 79MGS Nylon 6, 40% Glass Mineral reinforced 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.48 g/cc	0.0535 lb/in3	ASTM D792
吸水率	0.090 %	0.090 %	24 hrs; ASTM D570
平衡吸湿	1.5 %	1.5 %	50% RH; ASTM D570
饱和吸水率	4.0 %	4.0 %	ASTM D570
线性成型收缩率	0.0040 cm/cm	0.0040 in/in	ASTM D955

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	121	121	ASTM D785
抗张强度(屈服)	127 MPa	18400 psi	ASTM D638
伸长率 (断裂)	3.0 %	3.0 %	ASTM D638
弯曲模量	7.80 GPa	1130 ksi	ASTM D790
悬壁梁缺口冲击强度	0.480 J/cm	0.899 ft-lb/in	ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
电阻率	1.00e+14 ohm-cm	1.00e+14 ohm-cm	ASTM D257
介电常数	3.7 @Frequency 1e+6 Hz	3.7 @Frequency 1e+6 Hz	ASTM D150
介电强度	13.4 kV/mm	340 kV/in	ASTM D149

热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	218 °C	424 °F	ASTM D3418
载荷下热变形温度(0.46 MPa)	216 °C	421 °F	ASTM D648
载荷下热变形温度(1.8 MPa)	199 °C	390 °F	ASTM D648
可燃性(UL94)	HB	HB

如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!