PC EXL9330-8T7D1001 SABIC Lexan PC EXL9330物性

• Lexan PC EXL9330物性

• -60℃延展性,紫外稳定.耐燃性V-0/5VA. 非卤化,不含溴.

• Property

• TYPICAL PROPERTIES (1)
  MECHANICAL	Value	Unit	Standard
  Tensile Stress, yld, Type I, 50 mm/min	590	kgf/cm2	ASTM D 638
  Tensile Stress, brk, Type I, 50 mm/min	620	kgf/cm2	ASTM D 638
  Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D 638
  Tensile Strain, brk, Type I, 50 mm/min	130	%	ASTM D 638
  Tensile Modulus, 50 mm/min	21400	kgf/cm2	ASTM D 638
  Flexural Stress, yld, 1.3 mm/min, 50 mm span	900	kgf/cm2	ASTM D 790
  Flexural Modulus, 1.3 mm/min, 50 mm span	21000	kgf/cm2	ASTM D 790
  Tensile Stress, yield, 50 mm/min	55	MPa	ISO 527
  Tensile Stress, break, 50 mm/min	60	MPa	ISO 527
  Tensile Strain, yield, 50 mm/min	6	%	ISO 527
  Tensile Strain, break, 50 mm/min	125	%	ISO 527
  Tensile Modulus, 1 mm/min	2100	MPa	ISO 527
  Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
  Flexural Modulus, 2 mm/min	2200	MPa	ISO 178
  Hardness, H358/30	90	MPa	ISO 2039-1
  IMPACT	Value	Unit	Standard
  Izod Impact, notched, 23°C	81	cm-kgf/cm	ASTM D 256
  Izod Impact, notched, -30°C	69	cm-kgf/cm	ASTM D 256
  Izod Impact, notched, -50°C	59	cm-kgf/cm	ASTM D 256
  Izod Impact, notched, 23°C, 6.4mm	65	cm-kgf/cm	ASTM D 256
  Izod Impact, double-gated, 23°C	108	cm-kgf/cm	SABIC Method
  Instrumented Impact Total Energy, 23°C	539	cm-kgf	ASTM D 3763
  Izod Impact, unnotched 80*10*3 +23°C	NB	kJ/m2	ISO 180/1U
  Izod Impact, unnotched 80*10*3 -30°C	NB	kJ/m2	ISO 180/1U
  Izod Impact, notched 80*10*3 +23°C	70	kJ/m2	ISO 180/1A
  Izod Impact, notched 80*10*3 -30°C	55	kJ/m2	ISO 180/1A
  Izod Impact, notched 63.5*12.7*3.2, 23°C	80	kJ/m2	ISO 180/4A
  Izod Impact, notched 63.5*12.7*3.2, -30°C	65	kJ/m2	ISO 180/4A
  Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm	75	kJ/m2	ISO 179/1eA
  Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm	60	kJ/m2	ISO 179/1eA
  Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm	NB	kJ/m2	ISO 179/1eU
  Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm	NB	kJ/m2	ISO 179/1eU
  THERMAL	Value	Unit	Standard
  Vicat Softening Temp, Rate B/50	142	°C	ASTM D 1525
  HDT, 0.45 MPa, 3.2 mm, unannealed	134	°C	ASTM D 648
  HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D 648
  HDT, 1.82 MPa, 6.4 mm, unannealed	124	°C	ASTM D 648
  CTE, -40°C to 40°C, flow	6.66E-05	1/°C	ASTM E 831
  CTE, -40°C to 40°C, xflow	6.66E-05	1/°C	ASTM E 831
  CTE, 23°C to 80°C, flow	7.2E-05	1/°C	ISO 11359-2
  CTE, 23°C to 80°C, xflow	7.7E-05	1/°C	ISO 11359-2
  Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
  Vicat Softening Temp, Rate B/50	140	°C	ISO 306
  Vicat Softening Temp, Rate B/120	142	°C	ISO 306
  HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm	135	°C	ISO 75/Be
  HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm	124	°C	ISO 75/Ae
  Relative Temp Index, Elec	125	°C	UL 746B
  Relative Temp Index, Mech w/impact	115	°C	UL 746B
  Relative Temp Index, Mech w/o impact	120	°C	UL 746B
  PHYSICAL	Value	Unit	Standard
  Specific Gravity	1.18	-	ASTM D 792
  Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC Method
  Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC Method
  Melt Flow Rate, 300°C/1.2 kgf	10	g/10 min	ASTM D 1238
  Density	1.19	g/cm2	ISO 1183
  Water Absorption, (23°C/sat)	0.35	%	ISO 62
  Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
  Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm210 min	ISO 1133
  ELECTRICAL	Value	Unit	Standard
  Dielectric Strength, in oil, 3.2 mm	17	kV/mm	ASTM D 149
  Relative Permittivity, 50/60 Hz	2.95	-	ASTM D 150
  Relative Permittivity, 1 MHz	2.9	-	ASTM D 150
  Dissipation Factor, 50/60 Hz	0.0024	-	ASTM D 150
  Dissipation Factor, 1 MHz	0.0085	-	ASTM D 150
  Hot Wire Ignition {PLC)	1	PLC Code	UL 746A
  High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
  Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
  Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
  Surface Resistivity, ROA	>1.E+15	Ohm	IEC 60093
  Dielectric Strength, in oil, 3.2 mm	16	kV/mm	IEC 60243-1
  Relative Permittivity, 50/60 Hz	2.6	-	IEC 60250
  Relative Permittivity, 1 MHz	2.7	-	IEC 60250
  Dissipation Factor, 50/60 Hz	0.001	-	IEC 60250
  Dissipation Factor, 1 MHz	0.008	-	IEC 60250
  Comparative Tracking Index	225	V	IEC 60112
  FLAME CHARACTERISTICS	Value	Unit	Standard
  UL Recognized, 94V-0 Flame Class Rating (3)	1.49	mm	UL 94
  UL Recognized, 94-5VA Rating (3)	2.99	mm	UL 94
  Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
  Glow Wire Ignitability Temperature, 1.0 mm	825	°C	IEC 60695-2-13
  Oxygen Index (LOI)	35	%	ISO 4589
  UV-light, water exposure/immersion	F1	-	UL 746C

• Processing

• Parameter
  Injection Molding	Value	Unit
  Drying Temperature	120	°C
  Drying Time	3 - 4	hrs
  Drying Time (Cumulative)	48	hrs
  Maximum Moisture Content	0.02	%
  Melt Temperature	295 - 315	°C
  Nozzle Temperature	290 - 310	°C
  Front - Zone 3 Temperature	295 - 315	°C
  Middle - Zone 2 Temperature	280 - 305	°C
  Rear - Zone 1 Temperature	215 - 295	°C
  Mold Temperature	70 - 95	°C
  Back Pressure	0.3 - 0.7	MPa
  Screw Speed	40 - 70	rpm
  Shot to Cylinder Size	40 - 60	%
  Vent Depth	0.025 - 0.076	mm