1.25 g/cm3
ASTM D792
7.6 g/10min
280 °C
5 kg
ASTM D1238
7.6 g/10min
300 °C
5 kg
ASTM D1238
6.00 cm3/10min
280 °C
5 kg
ISO 1133
6.00 cm3/10min
300 °C
5 kg
ISO 1133
0.50 - 0.70 %
3.2 mm
Internal Method
f1
UL 746C
3650 MPa
5 mm/min
ASTM D638
4000 MPa
ISO 527-2/1
74.0 MPa
5 mm/min
Type I
ASTM D638
71.0 MPa
ISO 527-2
60.0 MPa
5 mm/min
Type I
ASTM D638
57.0 MPa
ISO 527-2
3.8 %
ASTM D638
3.7 %
ISO 527-2
8.4 %
5 mm/min
Type I
ASTM D638
11 %
ISO 527-2
3670 MPa
1.3 mm/min
50 mm span
ASTM D790
3550 MPa
2.6 mm/min
100 mm Span
ASTM D790
3800 MPa
ISO 178
117 MPa
ISO 178
117 MPa
2.6 mm/min
100 mm Span
ASTM D790
117 MPa
1.3 mm/min
50 mm span
ASTM D790
10 kJ/m2
23 °C
ISO 179/2C
130 J/m
23 °C
ASTM D256
9.0 kJ/m2
80*10*4 mm
23 °C
ISO 180/1A
2200 J/m
23 °C
ASTM D4812
810 J/m
3.2 mm
ASTM D256
443 J
23 °C
ASTM D3763
117 °C
0.45 MPa
3.2 mm
ASTM D648
128 °C
0.45 MPa
6.4 mm
ASTM D648
126 °C
0.45 MPa
120*10*4 mm
100 mm Span
4 mm
ISO 75-2/Be
108 °C
1.8 MPa
3.2 mm
ASTM D648
116 °C
1.8 MPa
6.4 mm
ASTM D648
111 °C
1.8 MPa
120*10*4 mm
100 mm Span
4 mm
ISO 75-2/Ae
132 °C
ISO 306/B50
136 °C
ISO 306/B120
7.1E-5 cm/cm/°C
-40 - 40 °C
ASTM E831
7.8E-5 cm/cm/°C
-40 - 40 °C
ASTM E831
100 °C
UL 746
85.0 °C
UL 746
100 °C
UL 746
V-0
1.5 mm
UL 94
5VA
2 mm
UL 94
960 °C
1 mm
IEC 60695-2-12
960 °C
2 mm
IEC 60695-2-12
960 °C
3 mm
IEC 60695-2-12
850 °C
1 mm
IEC 60695-2-13
800 °C
2 mm
IEC 60695-2-13
800 °C
3 mm
IEC 60695-2-13
TRUE
UL Unspecified
1.0E+16 ohms
ASTM D257
1.2e+16 ohms·cm
ASTM D257
17 kV/mm
3.2 mm
ASTM D149
2.89
60 Hz
ASTM D150
2.89
50 kHz
ASTM D150
2.70
1 MHz
ASTM D150
0.017
50 Hz
ASTM D150
0.017
60 Hz
ASTM D150
4.4E-3
1 MHz
ASTM D150
PLC 6
ASTM D495
PLC 2
UL 746
PLC 3
1.5 mm
UL 746
PLC 2
3 mm
UL 746
PLC 3
UL 746
PLC 0
1.5 mm
UL 746