1.29 g/cm3
DAM
ISO 1183
2.1 %
23 °C
50% RH
Equilibrium
DAM
ISO 62
6.8 %
23 °C
Saturation
DAM
immersed
ISO 62
0.0040 cm/cm
2 mm
DAM
ISO 294-4
0.012 cm/cm
2 mm
DAM
ISO 294-4
85
ISO 2039/2
102
ISO 2039/2
115
ISO 2039/2
122
ISO 2039/2
103 MPa
23 °C
ISO 527
159 MPa
23 °C
ISO 527
17.5 MPa
120 °C
Strain 0.53 %
ISO 527
18.5 MPa
90 °C
Strain 0.52 %
ISO 527
20.5 MPa
60 °C
Strain 0.52 %
ISO 527
22.2 MPa
120 °C
Strain 0.63 %
ISO 527
23.0 MPa
40 °C
Strain 0.48 %
ISO 527
24.5 MPa
90 °C
Strain 0.61 %
ISO 527
25.9 MPa
23 °C
Strain 0.44 %
ISO 527
26.2 MPa
60 °C
Strain 0.46 %
ISO 527
27.7 MPa
-20 °C
Strain 0.27 %
ISO 527
28.8 MPa
0 °C
Strain 0.33 %
ISO 527
30.6 MPa
120 °C
Strain 1.06 %
ISO 527
33.2 MPa
40 °C
Strain 0.36 %
ISO 527
33.4 MPa
90 °C
Strain 1.04 %
ISO 527
35.9 MPa
23 °C
Strain 0.25 %
ISO 527
37.4 MPa
60 °C
Strain 1.04 %
ISO 527
38.3 MPa
120 °C
Strain 1.26 %
ISO 527
40.4 MPa
120 °C
Strain 1.59 %
ISO 527
41.2 MPa
40 °C
Strain 0.96 %
ISO 527
42.0 MPa
90 °C
Strain 1.22 %
ISO 527
45.1 MPa
90 °C
Strain 1.56 %
ISO 527
45.4 MPa
60 °C
Strain 0.92 %
ISO 527
46.8 MPa
23 °C
Strain 0.88 %
ISO 527
47.6 MPa
120 °C
Strain 2.12 %
ISO 527
50.2 MPa
120 °C
Strain 1.89 %
ISO 527
50.7 MPa
60 °C
Strain 1.56 %
ISO 527
51.2 MPa
-20 °C
Strain 0.54 %
ISO 527
52.4 MPa
0 °C
Strain 0.66 %
ISO 527
52.8 MPa
120 °C
Strain 2.65 %
ISO 527
53.9 MPa
90 °C
Strain 2.08 %
ISO 527
55.4 MPa
40 °C
Strain 1.44 %
ISO 527
55.7 MPa
90 °C
Strain 1.83 %
ISO 527
56.5 MPa
120 °C
Strain 3.18 %
ISO 527
57.7 MPa
40 °C
Strain 0.72 %
ISO 527
58.8 MPa
120 °C
Strain 2.52 %
ISO 527
59.0 MPa
120 °C
Strain 3.71 %
ISO 527
60.0 MPa
23 °C
Strain 0.5 %
ISO 527
60.4 MPa
90 °C
Strain 2.6 %
ISO 527
60.7 MPa
120 °C
Strain 4.24 %
ISO 527
61.0 MPa
60 °C
Strain 1.38 %
ISO 527
61.1 MPa
60 °C
Strain 2.08 %
ISO 527
61.7 MPa
120 °C
Strain 4.77 %
ISO 527
62.2 MPa
120 °C
Strain 5.3 %
ISO 527
63.2 MPa
23 °C
Strain 1.32 %
ISO 527
64.5 MPa
120 °C
Strain 3.15 %
ISO 527
65.1 MPa
90 °C
Strain 3.12 %
ISO 527
66.0 MPa
90 °C
Strain 2.44 %
ISO 527
66.4 MPa
40 °C
Strain 1.92 %
ISO 527
68.1 MPa
120 °C
Strain 3.78 %
ISO 527
68.2 MPa
90 °C
Strain 3.64 %
ISO 527
68.8 MPa
60 °C
Strain 2.6 %
ISO 527
70.1 MPa
120 °C
Strain 4.41 %
ISO 527
70.3 MPa
90 °C
Strain 4.16 %
ISO 527
71.3 MPa
120 °C
Strain 5.04 %
ISO 527
71.4 MPa
90 °C
Strain 4.68 %
ISO 527
71.4 MPa
-20 °C
Strain 0.81 %
ISO 527
71.9 MPa
90 °C
Strain 5.2 %
ISO 527
72.0 MPa
0 °C
Strain 0.99 %
ISO 527
72.3 MPa
120 °C
Strain 5.67 %
ISO 527
72.7 MPa
120 °C
Strain 6.3 %
ISO 527
73.4 MPa
60 °C
Strain 1.84 %
ISO 527
73.5 MPa
90 °C
Strain 3.05 %
ISO 527
74.4 MPa
60 °C
Strain 3.12 %
ISO 527
74.8 MPa
40 °C
Strain 2.4 %
ISO 527
76.0 MPa
23 °C
Strain 1.76 %
ISO 527
77.8 MPa
40 °C
Strain 1.08 %
ISO 527
78.3 MPa
60 °C
Strain 3.64 %
ISO 527
78.7 MPa
90 °C
Strain 3.66 %
ISO 527
80.1 MPa
23 °C
Strain 0.75 %
ISO 527
80.9 MPa
60 °C
Strain 4.16 %
ISO 527
81.1 MPa
40 °C
Strain 2.88 %
ISO 527
81.9 MPa
90 °C
Strain 4.27 %
ISO 527
82.4 MPa
60 °C
Strain 4.68 %
ISO 527
83.0 MPa
60 °C
Strain 2.3 %
ISO 527
83.1 MPa
60 °C
Strain 5.2 %
ISO 527
83.6 MPa
90 °C
Strain 4.88 %
ISO 527
84.5 MPa
90 °C
Strain 5.49 %
ISO 527
84.8 MPa
90 °C
Strain 6.1 %
ISO 527
85.6 MPa
23 °C
Strain 2.2 %
ISO 527
85.7 MPa
40 °C
Strain 3.36 %
ISO 527
88.3 MPa
0 °C
Strain 1.32 %
ISO 527
89.0 MPa
-20 °C
Strain 1.08 %
ISO 527
89.0 MPa
40 °C
Strain 3.84 %
ISO 527
90.3 MPa
60 °C
Strain 2.76 %
ISO 527
91.2 MPa
40 °C
Strain 4.32 %
ISO 527
92.6 MPa
40 °C
Strain 4.8 %
ISO 527
92.8 MPa
23 °C
Strain 2.64 %
ISO 527
94.0 MPa
40 °C
Strain 1.44 %
ISO 527
95.6 MPa
60 °C
Strain 3.22 %
ISO 527
96.8 MPa
23 °C
Strain 1 %
ISO 527
98.0 MPa
23 °C
Strain 3.08 %
ISO 527
99.0 MPa
60 °C
Strain 3.68 %
ISO 527
102 MPa
60 °C
Strain 4.14 %
ISO 527
102 MPa
23 °C
Strain 3.52 %
ISO 527
102 MPa
0 °C
Strain 1.65 %
ISO 527
104 MPa
23 °C
Strain 3.96 %
ISO 527
104 MPa
60 °C
Strain 4.6 %
ISO 527
105 MPa
23 °C
Strain 4.4 %
ISO 527
105 MPa
-20 °C
Strain 1.35 %
ISO 527
107 MPa
40 °C
Strain 1.8 %
ISO 527
111 MPa
23 °C
Strain 1.25 %
ISO 527
114 MPa
0 °C
Strain 1.98 %
ISO 527
116 MPa
40 °C
Strain 2.16 %
ISO 527
118 MPa
-20 °C
Strain 1.62 %
ISO 527
122 MPa
23 °C
Strain 1.5 %
ISO 527
124 MPa
0 °C
Strain 2.31 %
ISO 527
124 MPa
40 °C
Strain 2.52 %
ISO 527
129 MPa
40 °C
Strain 2.88 %
ISO 527
131 MPa
-20 °C
Strain 1.89 %
ISO 527
132 MPa
0 °C
Strain 2.64 %
ISO 527
132 MPa
23 °C
Strain 1.75 %
ISO 527
133 MPa
40 °C
Strain 3.24 %
ISO 527
135 MPa
40 °C
Strain 3.6 %
ISO 527
139 MPa
0 °C
Strain 2.97 %
ISO 527
140 MPa
23 °C
Strain 2 %
ISO 527
142 MPa
-20 °C
Strain 2.16 %
ISO 527
145 MPa
0 °C
Strain 3.3 %
ISO 527
147 MPa
23 °C
Strain 2.25 %
ISO 527
153 MPa
-20 °C
Strain 2.43 %
ISO 527
155 MPa
23 °C
Strain 2.5 %
ISO 527
163 MPa
-20 °C
Strain 2.7 %
ISO 527
2.9 %
23 °C
ISO 527
7.0 %
23 °C
ISO 527
5.00 GPa
23 °C
ISO 527
7.30 GPa
23 °C
ISO 527
140 MPa
23 °C
ISO 178
210 MPa
23 °C
ISO 178
0.333 GPa
250 °C
ISO 6721
0.403 GPa
240 °C
ISO 6721
0.441 GPa
230 °C
ISO 6721
0.464 GPa
220 °C
ISO 6721
0.479 GPa
210 °C
ISO 6721
0.491 GPa
200 °C
ISO 6721
0.502 GPa
190 °C
ISO 6721
0.513 GPa
180 °C
ISO 6721
0.522 GPa
170 °C
ISO 6721
0.531 GPa
160 °C
ISO 6721
0.540 GPa
150 °C
ISO 6721
0.549 GPa
140 °C
ISO 6721
0.558 GPa
130 °C
ISO 6721
0.570 GPa
120 °C
ISO 6721
0.587 GPa
110 °C
ISO 6721
0.614 GPa
100 °C
ISO 6721
0.659 GPa
90 °C
ISO 6721
0.730 GPa
80 °C
ISO 6721
0.841 GPa
70 °C
ISO 6721
1.015 GPa
60 °C
ISO 6721
1.28 GPa
50 °C
ISO 6721
1.424 GPa
40 °C
ISO 6721
1.509 GPa
30 °C
ISO 6721
1.564 GPa
20 °C
ISO 6721
1.606 GPa
10 °C
ISO 6721
1.63 GPa
0 °C
ISO 6721
1.643 GPa
-10 °C
ISO 6721
1.653 GPa
-20 °C
ISO 6721
1.67 GPa
-30 °C
ISO 6721
1.699 GPa
-40 °C
ISO 6721
1.745 GPa
-50 °C
ISO 6721
7.00 kJ/m2
-30 °C
ISO 180-1A
7.00 kJ/m2
-30 °C
ISO 180-1A
8.00 kJ/m2
23 °C
ISO 180-1A
9.00 kJ/m2
23 °C
ISO 180-1A
4.50 J/cm2
-30 °C
ISO 179/1eU
5.00 J/cm2
-30 °C
ISO 179/1eU
5.50 J/cm2
23 °C
ISO 179/1eU
7.50 J/cm2
23 °C
ISO 179/1eU
0.900 J/cm2
23 °C
ISO 179/1eA
0.900 J/cm2
-30 °C
ISO 179/1eA
0.900 J/cm2
-30 °C
ISO 179/1eA
0.950 J/cm2
23 °C
ISO 179/1eA
4700 MPa
23 °C
ISO 899
3100 MPa
23 °C
ISO 899
500 μm/m-°C
23 - 55 °C
DAM
ASTM E831
111 μm/m-°C
23 - 55 °C
DAM
ASTM E831
263 °C
10°C/min
DAM
ISO 11357-1/-3
260 °C
0.46 MPa
DAM
ISO 75-1/-2
242 °C
1.8 MPa
DAM
ISO 75-1/-2
80.0 °C
10°C/min
DAM
ISO 11357-1/-2
140 °C
0.71 mm
DAM
UL 746B
140 °C
3 mm
DAM
UL 746B
HB
3 mm
DAM
IEC 60695-11-10
HB
0.71 mm
DAM
IEC 60695-11-10
HB
1.5 mm
DAM
IEC 60695-11-10
1.00e+11 ohms·cm
23 °C
50% RH
IEC 60093
= 1.00e+15 ohms·cm
23 °C
DAM
IEC 60093
= 1.00e+17 ohms·cm
23 °C
DAM
IEC 60093
1.00e+12 ohm
23 °C
50%RH
IEC 60093
= 1.00e+15 ohm
23 °C
DAM
IEC 60093
3.9
23 °C
Frequency 1000000 Hz
DAM
IEC 60250
4.4
23 °C
Frequency 1000000 Hz
50% RH
IEC 60250
0.016
23 °C
Frequency 1000000 Hz
DAM
IEC 60250
0.070
23 °C
Frequency 1000000 Hz
50%RH
IEC 60250
400 V
23 °C
DAM
IEC 60112