BASF Ultrason? E 2010 C6 30% Carbon Filled

Polymer,Thermoplastic,Polysulfone (PSU),Polyphenylsulfone, Glass or Carbon Fiber Reinforced

BASF

产品说明:

Carbon fibers and Ultrason? two partners with good properties. The combination of carbon fibers with the amorphous high-temperature plastic Ultrason? guarantees mechanical properties for temperatures of up to 200 °C.

Excellent properties: very high stiffness, very constant mechanical properties, low and constant thermal expansion = dimensionally stable and excellent creep behavior

Potential applications: Substitution of metal, using the advantages of thermoplastic materials (e.g. realization of complex designs by injection-molding), substitution of PEEK for applications with a maximum of 200 °C, parts with antistatic requirements and parts with electrically conductive requirements

Information provided by BASF

会员资料

公司名称:

联系人:

公司地址:

完善资料

附加功能

PDF物性文档 [普通版本][带会员联系方式版本]

BASF Ultrason? E 2010 C6 30% Carbon Filled 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
体积密度	0.700 - 0.800 g/cc	0.0253 - 0.0289 lb/in3
密度	1.47 g/cc	0.0531 lb/in3	ISO 1183
吸水率	= 1.7 %	= 1.7 %	Equilibrium; ISO 62
平衡吸湿	0.60 %	0.60 %	23°C; 50% RH; ISO 62
粘度测量	56	56	[cmsup3/sup/g]; ISO 1628
线性成型收缩率,Flow	0.0015 cm/cm	0.0015 in/in	ISO 294
线性成型收缩率，横向	0.0035 cm/cm	0.0035 in/in	ISO 294
熔体流动速率	= 22.05 g/10 min @Load 10.0 kg, Temperature 360 °C	= 22.05 g/10 min @Load 22.0 lb, Temperature 680 °F	ISO 1133
	= 45 g/10 min @Load 10.0 kg, Temperature 400 °C	= 45 g/10 min @Load 22.0 lb, Temperature 752 °F

机械性能	额定值 (公制)	额定值 (英制)	测试方法
球压硬度	227 MPa @Load 36.5 kg, Time 30.0 sec	32900 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
抗张强度(断裂)	185 MPa	26800 psi	5 mm/min; ISO 527-2
抗张强度(屈服)	185 MPa	26800 psi	50 mm/min; ISO 527-2
伸长率 (断裂)	1.5 %	1.5 %	5mm/min; ISO 527-2
屈服伸长率	1.5 %	1.5 %	50 mm/min; ISO 527-2
	0.21 % @Time 3600 sec, Pressure 50.0 MPa	0.21 % @Time 1.00 hour, Pressure 7250 psi	ISO 899
	0.23 % @Pressure 50.0 MPa, Time 360000 sec	0.23 % @Pressure 7250 psi, Time 100 hour	ISO 899
	0.24 % @Pressure 50.0 MPa, Time 3.60e+6 sec	0.24 % @Pressure 7250 psi, Time 1000 hour	ISO 899
	0.38 % @Time 3600 sec, Pressure 70.0 MPa	0.38 % @Time 1.00 hour, Pressure 10200 psi	ISO 899
	0.40 % @Pressure 70.0 MPa, Time 360000 sec	0.40 % @Pressure 10200 psi, Time 100 hour	ISO 899
	0.40 % @Pressure 70.0 MPa, Time 3.60e+6 sec	0.40 % @Pressure 10200 psi, Time 1000 hour	ISO 899
	0.50 % @Time 3600 sec, Pressure 90.0 MPa	0.50 % @Time 1.00 hour, Pressure 13100 psi	ISO 899
	0.55 % @Pressure 90.0 MPa, Time 360000 sec	0.55 % @Pressure 13100 psi, Time 100 hour	ISO 899
	0.58 % @Pressure 90.0 MPa, Time 3.60e+6 sec	0.58 % @Pressure 13100 psi, Time 1000 hour	ISO 899
	0.60 % @Time 3600 sec, Pressure 110 MPa	0.60 % @Time 1.00 hour, Pressure 16000 psi	ISO 899
	0.70 % @Time 360000 sec, Pressure 110 MPa	0.70 % @Time 100 hour, Pressure 16000 psi	ISO 899
	0.75 % @Pressure 110 MPa, Time 3.60e+6 sec	0.75 % @Pressure 16000 psi, Time 1000 hour	ISO 899
	0.80 % @Time 3600 sec, Pressure 130 MPa	0.80 % @Time 1.00 hour, Pressure 18900 psi	ISO 899
	0.90 % @Time 360000 sec, Pressure 130 MPa	0.90 % @Time 100 hour, Pressure 18900 psi	ISO 899
	0.98 % @Pressure 130 MPa, Time 3.60e+6 sec	0.98 % @Pressure 18900 psi, Time 1000 hour	ISO 899
拉伸模量	= 13.0 GPa @Temperature 200 °C	= 1890 ksi @Temperature 392 °F
	= 20.0 GPa @Temperature 150 °C	= 2900 ksi @Temperature 302 °F
	= 21.0 GPa @Temperature 100 °C	= 3050 ksi @Temperature 212 °F
	= 22.0 GPa @Temperature 50.0 °C	= 3190 ksi @Temperature 122 °F	ISO 527-2
剪切模量	0.200 GPa @Temperature 225 °C	29.0 ksi @Temperature 437 °F	ISO 6721
	0.900 GPa @Temperature 200 °C	131 ksi @Temperature 392 °F	ISO 6721
	0.950 GPa @Temperature 100 °C	138 ksi @Temperature 212 °F	ISO 6721
	1.00 GPa @Temperature 50.0 °C	145 ksi @Temperature 122 °F	ISO 6721
悬壁梁缺口冲击强度	8.00 kJ/m2	3.81 ft-lb/in2	ISO 180/A
	7.00 kJ/m2 @Temperature -30.0 °C	3.33 ft-lb/in2 @Temperature -22.0 °F	ISO 180/A
简支梁无缺口冲击强度	4.00 J/cm2	19.0 ft-lb/in2	ISO 179/1eU
	4.00 J/cm2 @Temperature -30.0 °C	19.0 ft-lb/in2 @Temperature -22.0 °F	ISO 179/1eU
简支梁缺口冲击强度	0.750 J/cm2	3.57 ft-lb/in2	ISO 179/1eA
	0.650 J/cm2 @Temperature -30.0 °C	3.09 ft-lb/in2 @Temperature -22.0 °F	ISO 179/1eA