PPS FORTRON 1140L4
| 价格 | ￥55.00/公斤 | ￥53.00/公斤 |
| 起订量 | ≥25 | ≥500 |
| 所在地 | 广东 东莞 | 可售量 5000公斤 |
产品推荐
基本参数
| 牌号 | 1140L4 | 厂商 | FORTRON |
| 厂家(产地) | 美国泰科纳 | 特性级别 | 超高韧性，刚性，高 |
| 用途级别 | 电气/电子应用领域，阀门/阀门部件 | 类型 | 正牌料 |
| 规格级别 | 25/KG | 颜色 | 本色，黑色 |
Fortron 1140L4
聚苯硫醚
40% 玻璃纤维增强材料
Celanese Corporation
产品说明：
Fortron 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).
Fortron 1140L4 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 多点数据 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.65 | g/cm3 | ASTM D792, ISO 1183 |
| 特定体积 | 0.611 | cm3/g | ASTM D792 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1500 | J/kg/°C | 内部方法 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Specimen Thickness - Shrinkage | 3.18 | mm | 内部方法 |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 收缩率 | |||
| 流动 | 0.20 到 0.30 | % | ASTM D955 |
| 横向流动 | 0.50 到 0.70 | % | ASTM D955 |
| 垂直流动方向 | 0.40 到 0.60 | % | ISO 294-4 |
| 流动方向 | 0.20 到 0.60 | % | ISO 294-4 |
| 吸水率(饱和, 23°C) | 0.020 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 | |||
| M 级 | 100 | ASTM D785 | |
| M 计秤 | 100 | ISO 2039-2 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| -40°C | 14500 | MPa | ASTM D638 |
| 75°C | 11900 | MPa | ASTM D638 |
| 150°C | 4270 | MPa | ASTM D638 |
| 200°C | 3240 | MPa | ASTM D638 |
| -- | 14700 | MPa | ISO 527-2/1A/1 |
| 抗张强度 | |||
| 断裂, 23°C | 200 | MPa | ASTM D638 |
| 断裂 | 195 | MPa | ISO 527-2/1A/5 |
| 伸长率 | |||
| 断裂, 23°C | 1.7 | % | ASTM D638 |
| 断裂 | 1.9 | % | ISO 527-2/1A/5 |
| 弯曲模量(23°C) | 14500 | MPa | ISO 178 |
| 弯曲应力1 | 285 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m2 | ISO 179/1eA |
| 23°C | 10 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| -30°C | 53 | kJ/m2 | ISO 179/1eU |
| 23°C | 53 | kJ/m2 | ISO 179/1eU |
| 悬壁梁缺口冲击强度 | ISO 180/1A | ||
| -30°C | 10 | kJ/m2 | ISO 180/1A |
| 23°C | 10 | kJ/m2 | ISO 180/1A |
| 无缺口伊佐德冲击强度(23°C) | 34 | kJ/m2 | ISO 180/1U |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | |||
| 0.45 MPa, 退火 | 280 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 265 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 270 | °C | ISO 75-2/A |
| 8.0 MPa, 未退火 | 215 | °C | ISO 75-2/C |
| 玻璃转化温度2 | 90.0 | °C | ISO 11357-2 |
| 熔融温度3 | 280 | °C | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度 | 28 | kV/mm | IEC 60243-1 |
| 介电常数 | |||
| 1 kHz | 3.50 | ASTM D150 | |
| 1 MHz | 3.50 | ASTM D150 | |
| 1 MHz | 4.60 | IEC 60250 | |
| 耗散因数 | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 6.2E-3 | IEC 60250 | |
| 耐电弧性 | 134 | sec | ASTM D495 |
| 漏电起痕指数 | 125 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 0.380 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| 极限氧指数 | 47 | % | ISO 4589-2 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 130 到 140 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 20.0 到 30.0 | °C | |
| 料筒后部温度 | 290 到 300 | °C | |
| 料筒中部温度 | 310 到 320 | °C | |
| 料筒前部温度 | 330 到 340 | °C | |
| 射嘴温度 | 310 到 330 | °C | |
| 加工（熔体）温度 | 330 到 340 | °C | |
| 模具温度 | 140 到 160 | °C | |
| 注塑压力 | 50.0 到 100 | MPa | |
| 注射速度 | 快速 | ||
| 保压 | 30.0 到 70.0 | MPa | |
| 背压 | 0.00 到 3.00 | MPa |
| 注射说明 |
|---|
东莞市崀峰塑胶原料有限公司
联系人：
周先生
服务热线：
ꢖ렙댦펗렙댦ꊑ렙ꢖ펗ꢖ
ꊑ-ꝡ-ꊑꝡꊑꢖ렙
公司地址：
东莞市常平镇麦元村大京九塑胶原料市场塑招东路697号
-
朗盛 POCAN PBT/PET ECO T 3240 000000￥0元
-
POCAN PBT/PET-GF45% ECO T3240￥0元
-
朗盛 POCAN PBT/PET ECO T 3230 000000￥0元
-
POCAN PBT/PET玻纤 ECO T3230￥0元
-
宝理 DURANEX >PBT/PET-GF55%
-
宝理 DURANEX 抗紫外线PBT/PET CN7740XB￥0元
-
供应PBT/PET POCAN 朗盛 T3150 XF￥0元
-
PA66 Ultramid® 1403-2 BK ND3007￥0元
PPS FORTRON 1140L4 相关产品
- PC/ABS 上海科思创（拜耳） FR2010工程塑胶原料厂家
- PC/ABS 韩国LG GN-5001RF工程塑胶原料
- PC/ABS 韩国LG GN5001RFH工程塑胶型号
- PC/ABS 韩国LG GN-5001RFH工程塑胶原料批发
- PC/ABS 韩国LG GN-5008HF工程塑胶原料厂家
- PC/ABS 韩国LG GN-5101RF工程塑胶型号
- PC/ABS 韩国LG GN-5301F工程塑胶原料
- 工程塑胶原料批发PC/ABS 韩国LG GP-5006AF
- PC/ABS 韩国LG GP-5006BH工程塑胶原料厂家
- 塑料PC/ABS 上海科思创（拜耳） FR-3000塑胶原料
- 工程塑胶型号PC/ABS 韩国LG GP-5106F
- V-0阻燃级PC/ABS塑胶原料韩国LG GP-5306F
- 玻纤增强塑胶原料PC/ABS 广州LG ER-5001RFA注塑级
- 注塑级塑胶原料PC/ABS 广州LG ER-5001RF
- 阻燃塑胶原料PC/ABS 广州LG EC-5000AF抗静电 注塑级
- 耐热性塑胶原料PC/ABS 韩国LG HR-5007A
- 高抗冲塑胶原料PC/ABS 韩国LG MP-5000AM
- 耐低温塑胶原料PC/ABS 韩国LG HR-5006A
猜你在找
- 高耐冲击PPS 6150T6 HF2000 HD9100 PPS-I-(GF+MD)50
- PPS 6165A4 HF2000 HD9050 HD9100 PPS-(GF+MD)65 PPS 6165A6
- PPS 6165A7 HF2000/HD9100 PPS-(GF+MD)60
- PPS 6345A4 HF2000 HD9050 PPS+PTFE-GF30
- PPS 6465A6 HF2000 HD9050 PPS-(GF+GB)65 PPS 6465A62
- PPS 6565A6 HF2000 HD9050 PPS 6565A7 HD9050
- 导电PPS 7140A4 HD9000 PPS+PTFE+CF30
- 导电PPS 7340A4 HD9000 PPS-(GF+MD+CD)45
- 导电PPS 2130A1 HD9000 PPS+CF30 PPS加碳纤30%
- PPS 3130A1 HF2000 HD9100 PPS+MH30
- 电子电器 连接器PPS 日本东丽 A503 注塑级
- PPS 1130A64 HD9100 PPS+GF30% 加30%玻纤PPS
免责声明：以上展示的PPS FORTRON 1140L4 信息由东莞市崀峰塑胶原料有限公司自行提供，内容的真实性、准确性和合法性由发布企业负责，
全球塑胶网对此不承担责任。
风险防范建议：为保障您的利益，建议优先选择速购通会员
手机版：PPS FORTRON 1140L4
更新产品链接为：https://www.51pla.com/html/sellinfo/456/45656438.htm
发送询价单