产品推荐
PEI 美国基础创新 ULTEM? Resin 1010P
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.27
|
g/cm3
|
ASTM D792,ISO 1183 |
|
熔流率（熔体流动速率）(337°C/6.6 kg)
|
18
|
g/10 min
|
ASTM D1238 |
|
熔融体积流量（MVR）
|
ISO 1133 | ||
|
340°C/5.0 kg
|
13
|
cm3/10min
|
|
|
360°C/5.0 kg
|
25
|
cm3/10min
|
|
|
吸水率
|
|||
|
24 hr, 23°C
|
0.25
|
%
|
ASTM D570,ISO 62 |
|
饱和, 23°C
|
1.3
|
%
|
ASTM D570,ISO 62 |
|
平衡, 23°C, 50% RH1
|
0.20
|
%
|
ISO 62 |
|
平衡, 23°C, 50% RH
|
0.70
|
%
|
ISO 62 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
|||
|
M 级
|
109
|
ASTM D785 | |
|
M 计秤
|
106
|
ISO 2039-2 | |
|
球压硬度(H 358/30)
|
140
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--2
|
3350
|
MPa
|
ASTM D638 |
|
--
|
3200
|
MPa
|
ISO 527-1/1 |
|
抗张强度
|
|||
|
屈服3
|
115
|
MPa
|
ASTM D638 |
|
屈服4
|
110
|
MPa
|
ASTM D638 |
|
屈服
|
110
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
7.0
|
%
|
ASTM D638 |
|
屈服3
|
7.0
|
%
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
60
|
%
|
ASTM D638 |
|
断裂3
|
60
|
%
|
ASTM D638 |
|
断裂
|
50
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
3200
|
MPa
|
ASTM D790 |
|
100 mm 跨距6
|
3400
|
MPa
|
ASTM D790 |
|
--7
|
3300
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--7,8
|
160
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
165
|
MPa
|
ASTM D790 |
|
屈服, 100 mm 跨距6
|
160
|
MPa
|
ASTM D790 |
|
泊松比
|
0.36
|
ASTM E132 | |
|
泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度9
|
ISO 179/1eA | ||
|
-30°C
|
4.0
|
kJ/m2
|
|
|
23°C
|
4.0
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
41
|
J/m
|
ASTM D256 |
|
23°C
|
32
|
J/m
|
ASTM D256 |
|
-30°C10
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
23°C10
|
5.0
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
-30°C
|
1500
|
J/m
|
ASTM D4812 |
|
23°C
|
1600
|
J/m
|
ASTM D4812 |
|
-30°C10
|
无断裂
|
ISO 180/1U | |
|
23°C10
|
无断裂
|
ISO 180/1U | |
|
反向缺口冲击(3.20 mm)
|
1200
|
J/m
|
ASTM D256 |
|
落锤冲击(23°C)
|
33.0
|
J
|
内部方法 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
207
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 6.40 mm
|
210
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10
|
209
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
190
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
201
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10
|
192
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
211
|
°C
|
ASTM D152511,ISO 306/B5011 |
|
--
|
212
|
°C
|
ISO 306/B120 |
|
--
|
215
|
°C
|
ISO 306/A50 |
|
Ball Pressure Test(123 到 127°C)
|
通过
|
IEC 60695-10-2 | |
|
线形热膨胀系数
|
|||
|
流动 : -20 到 150°C
|
5.6E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -20 到 150°C
|
5.2E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -20 到 150°C
|
5.4E-5
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -20 到 150°C
|
5.2E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
导热系数
|
0.22
|
W/m/K
|
ASTM C177,ISO 8302 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohms
|
IEC 60093 |
|
体积电阻率
|
|||
|
--
|
1.0E+17
|
ohms·cm
|
ASTM D257 |
|
--
|
1.0E+15
|
ohms·cm
|
IEC 60093 |
|
介电强度
|
|||
|
1.60 mm, in Air
|
33
|
kV/mm
|
ASTM D149 |
|
1.60 mm, in Oil
|
28
|
kV/mm
|
ASTM D149 |
|
3.20 mm, in Oil
|
20
|
kV/mm
|
ASTM D149 |
|
0.800 mm, 在油中
|
33
|
kV/mm
|
IEC 60243-1 |
|
1.60 mm, 在油中
|
25
|
kV/mm
|
IEC 60243-1 |
|
3.20 mm, 在油中
|
16
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
100 Hz
|
3.15
|
ASTM D150 | |
|
1 kHz
|
3.15
|
ASTM D150 | |
|
1.10 GHz
|
3.01
|
内部方法 | |
|
5.00 GHz
|
3.02
|
内部方法 | |
|
10.0 GHz
|
3.02
|
内部方法 | |
|
50 Hz
|
2.90
|
IEC 60250 | |
|
60 Hz
|
2.90
|
IEC 60250 | |
|
1 MHz
|
2.90
|
IEC 60250 | |
|
耗散因数
|
|||
|
100 Hz
|
1.5E-3
|
ASTM D150 | |
|
1 kHz
|
1.2E-3
|
ASTM D150 | |
|
1.10 GHz
|
1.2E-3
|
内部方法 | |
|
5.00 GHz
|
2.4E-3
|
内部方法 | |
|
10.0 GHz
|
2.7E-3
|
内部方法 | |
|
50 Hz
|
5.0E-4
|
IEC 60250 | |
|
60 Hz
|
5.0E-4
|
IEC 60250 | |
|
1 MHz
|
6.0E-3
|
IEC 60250 | |
|
漏电起痕指数
|
IEC 60112 | ||
|
--
|
150
|
V
|
|
|
解决方案 B
|
100
|
V
|
|
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
极限氧指数
|
44
|
%
|
ASTM D2863 |
上海正逢塑胶有限公司
联系人：
王总
服务热线：
퍹쁅퍹넠퍹쁅핲
퍹쁅퍹넠퍹쁅핲
公司地址：
上海市青浦区公园路99号舜浦大厦7层o区744室
-
供应 台湾奇美 PA-765 高流动阻燃级abs 高刚性￥22.74元
-
美国杜邦 FR52G30BL 高刚性高强度 玻璃纤维增强30% 耐高温尼龙￥55.66元
-
VALOX沙伯基础 3706 冲击改性pc/pbt 高强度高韧性 耐化学性￥35.08元
-
供应 美国杜邦 103FHS 热稳定pa66 耐高温 高温线材原料 抗老化￥37.24元
-
供应 ABS 台湾奇美 PA-777E 热稳定性 耐高温 抗静电￥20.19元
-
现货供应 ps66 日本旭化成 1300G 抗蠕变性 耐疲劳 玻纤增强30%￥35.77元
-
供应 PC 沙伯基础 DFL-4032 耐磨损 耐候 高强度 自润滑性￥55.66元
-
供应 沙伯基础 EXL1132T 耐温低耐寒pc 高流动 抗紫外线稳定￥50.96元
PEI 美国基础创新 ULTEM™ Resin 1010P 耐热性 水解稳定 耐化学品相关产品
- 特种塑料PEI/沙伯基础(原GE)/4001(耐磨) 加PTFE超耐磨原料塑料
- PEI 2100 沙伯基础(原GE) 注塑级 玻纤增强10% 20 耐高温 耐冲击
- PEI 1000 基础创新 琥珀色 耐高温 耐化学 高韧性 pei塑胶原料
- 玻纤增强20%聚醚酰亚胺PEI塑料 沙伯基础(原GE) 2200阻燃V0耐高温PEI塑料原料
- 进口原装PEI 沙伯基础(原GE) 2100纤维增强 注塑级 阻燃级pei塑料原料
- 热稳定优质PEI塑料 沙伯基础(原GE)/2310 30%玻纤增强PEI 低粘度现货
- 进口原装PEI塑料原料 沙伯基础(原GE) 2100纤维增强 注塑级 阻燃级pei塑料原料
- 提供优质PEI塑料 沙伯基础(原GE) 2300玻纤增强30% 阻燃V0 PEI塑料原料
- 代理沙伯基础PEI ULTEM 1000-7101SABIC
- 代理沙伯基础PEI ULTEM 1000-1000 SABIC
- 代理沙伯基础PEI ULTEM 1000E SABIC
- 代理沙伯基础PEI ULTEM 1000R SABIC 纯树脂
- 代理沙伯基础PEI ULTEM 1000F SABIC 食品级
- 代理沙伯基础PEI ULTEM 1000FC SABIC
- 代理沙伯基础PEI ULTEM 1000RV SABIC 食品级
- 代理沙伯基础PEI ULTEM 1000P SABIC
- 代理沙伯基础PEI ULTEM 1010-7101 SABIC
- 代理沙伯基础PEI ULTEM 1010-1000 SABIC
猜你在找
- PEI 基础创新塑料 美国 1000 注塑-高刚性-耐高温-耐磨
- PEI 基础创新塑料 美国 1000 8140注塑-高刚性-耐高温-耐磨
- PEI 基础创新塑料 美国 1000 GN7E6358耐高温-耐磨
- PEI 基础创新塑料 美国 1000 GY
- PEI 基础创新塑料 美国 1000 WH
- PEI 基础创新塑料 美国 1000-7118 耐高温阻燃
- PEI 基础创新塑料 美国 1000F-7005
- 现货原包PEI 基础创新塑料 美国1000P-1000热稳定
- PEI 基础创新塑料 美国1000-GY6B416热稳定
- PEI 基础创新塑料(美国) PEI 1000-GY6B416
- PEI 基础创新塑料 美国 1000-1100
- PEI 基础创新塑料 美国 1000F-7101耐高温阻燃PEI
免责声明：以上展示的PEI 美国基础创新 ULTEM™ Resin 1010P 耐热性 水解稳定 耐化学品信息由上海正逢塑胶有限公司自行提供，内容的真实性、准确性和合法性由发布企业负责，
全球塑胶网对此不承担责任。
风险防范建议：为保障您的利益，建议优先选择速购通会员
手机版：PEI 美国基础创新 ULTEM™ Resin 1010P 耐热性 水解稳定 耐化学品
更新产品链接为：https://www.51pla.com/html/sellinfo/471/47153675.htm
发送询价单