Kingfa JH950-402 ABS PC

Kingfa JH950-502 ABS PC

Kingfa JH950-602 ABS PC

Kingfa JH960 6100 ABS PC

Kingfa JH960 6111 ABS PC

Kingfa JH960 6300 ABS PC

Kingfa JH960 6610 ABS PC

Kingfa JH960 HT10 ABS PC

Kingfa JH-R0G30 ABS PC

Kingfa JH-R2G10 P60 ABS PC

Kingfa MAC-301 ABS PC

Kingfa MAC-451 UV ABS PC

Kingfa MAC-451 ABS PC

Kingfa MAC-451PG ABS PC

Kingfa MAC-501 ABS PC

Kingfa MAC-501DY ABS PC

Kingfa MAC-551 ABS PC

Kingfa MAC-601 AC ABS PC

Kingfa MAC-601 DY ABS PC

Kingfa MAC-601 UV ABS PC

Kingfa MAC-601 ABS PC

Kingfa MAC-701 ABS PC

Kingfa MAC-751 HF ABS PC

Kingfa MAC-751 ABS PC

Kingfa MAC-851 ABS PC

Kingfa NH-627 ABS

Kingfa JH950-502 Low-temperature Resistant Flame Retardant PC/ABS Alloy

Polymer,Thermoplastic,ABS Polymer,Polycarbonate/ABS Alloy, Unreinforced,Polycarbonate (PC)

Kingfa Sci. amp; Tech. Co.

产品说明:

Features:
• UL V-0 @ 3.2mm
• Excellent balance properties
• Good low temperature resistance
• Good normal/low temperature impact strength
• Good surface

Applications:
• Controller
• Plug
• Socket
• Shell of ammeter

Information Provided by Kingfa Sci. Tech. Co., Ltd.

Kingfa JH950-502 Low-temperature Resistant Flame Retardant PC/ABS Alloy 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.14 g/cc @Temperature 23.0 °C	1.14 g/cc @Temperature 73.4 °F	ASTM D792
吸水率	0.15 % @Temperature 23.0 °C, Time 86400 sec	0.15 % @Temperature 73.4 °F, Time 24.0 hour	ASTM D570
线性成型收缩率	0.0040 - 0.0060 cm/cm @Temperature 23.0 °C	0.0040 - 0.0060 in/in @Temperature 73.4 °F	ASTM D955

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	115	115	ASTM D785
抗张强度(断裂)	= 50.0 MPa	= 7250 psi	50mm/min; ASTM D638
伸长率 (断裂)	= 40 %	= 40 %	50mm/min; ASTM D638
弯曲强度	80.0 MPa	11600 psi	2mm/min; ASTM D790
弯曲模量	2.35 GPa	341 ksi	2mm/min; ASTM D790
悬壁梁缺口冲击强度	3.80 J/cm @Thickness 3.20 mm, Temperature -40.0 °C	7.12 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F	ASTM D256
	4.80 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	8.99 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
表面电阻	1.00e+15 ohm	1.00e+15 ohm	ASTM D257
介电强度	28.0 kV/mm	711 kV/in	1.6mm; ASTM D149

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(0.46 MPa)	123 °C @Thickness 6.40 mm	253 °F @Thickness 0.252 in	ASTM D648
载荷下热变形温度(1.8 MPa)	110 °C @Thickness 6.40 mm	230 °F @Thickness 0.252 in	ASTM D648
可燃性(UL94)	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	= 265 °C	= 509 °F
料筒后部温度	210 - 240 °C	410 - 464 °F	Start Point: 215°C
料筒中部温度	220 - 240 °C	428 - 464 °F	Start Point: 225°C
料筒前部温度	220 - 250 °C	428 - 482 °F	Start Point: 235°C
加工（熔体）温度	220 - 255 °C	428 - 491 °F	Start Point: 230°C
模具温度	60.0 - 80.0 °C	140 - 176 °F	Start Point: 70°C
干燥温度	100 - 110 °C @Time 14400 - 21600 sec	212 - 230 °F @Time 4.00 - 6.00 hour	Pre-dry
背压	0.000 - 1.00 MPa	0.000 - 145 psi

材料描述		测试方法
射速	60-100%