PA66 Vydyne/首诺 (奥升德) ECO315无卤阻燃 韧性 延展性

PA66物性表 Ascend美国首诺Vydyne ECO-315物性表

Ascend Vydyne? ECO-315 Nylon 66（聚氨酯-尼龙66） 本物性表由中国塑商之家www.plas-cn.com塑料网提供，转载请注明来源！
Physical Properties物理性质	Metric公制数据	English英制数据	Comments测试方法
Specific Gravity比重	1.16g/cc	1.16g/cc	ISO 1183
Water Absorption吸水率	0.80 %	0.80 %	24 hrs; ISO 62
Moisture Absorption at Equilibrium吸湿平衡	1.8 %	1.8 %	Equilibrium at 50%rh; ISO 62
Linear Mold Shrinkage线性收缩率	0.012cm/cm @Thickness 2.00 mm	0.012in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse线性收缩率/横向	0.014cm/cm @Thickness 2.00 mm	0.014in/in @Thickness 0.0787 in	ISO 294-4
Mechanical Properties力学性能	Metric公制数据	English英制数据	Comments测试方法
Tensile Strength, Yield屈服拉伸强度	75.0MPa	10900psi	ISO 527
Elongation at Break断裂伸长率	25 %	25 %	ISO 527
Elongation at Yield屈服伸长率	5.5 %	5.5 %	ISO 527
Tensile Modulus拉伸模量	5.00GPa	725ksi	ISO 527
Flexural Strength弯曲强度	92.0MPa	13300psi	ISO 178
Flexural Modulus弯曲弹性模量	3.20GPa	464ksi	ISO 178
Poissons Ratio泊松比	0.41	0.41	ISO 527
Shear Modulus剪切模量	1.77GPa	257ksi	Calculated
Izod Impact, Notched悬臂梁缺口冲击强度(ISO)	6.00kJ/m2	2.86ft-lb/in2	ISO 180
Charpy Impact Unnotched夏比缺口试样冲击	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
Charpy ImPAct, Notched夏比缺口冲击	0.540J/cm2 @Temperature 23.0 °C	2.57ft-lb/in2 @Temperature 73.4 °F	ISO 179
	0.540J/cm2 @Temperature -30.0 °C	2.57ft-lb/in2 @Temperature -22.0 °F	ISO 179
Electrical Properties电性能	Metric公制数据	English英制数据	Comments测试方法
Volume ResiSTivity体积电阻率	3.00e+15ohm-cm @Thickness 3.00 mm	3.00e+15ohm-cm @Thickness 0.118 in	IEC 60093
Dielectric Strength介电强度	16.3kV/mm @Thickness 3.00 mm	414kV/in @Thickness 0.118 in	step by step; IEC 60243
	26.3kV/mm @Thickness 1.00 mm	668kV/in @Thickness 0.0394 in	step by step; IEC 60243
High Voltage Arc Resistance to Ignition高压电弧电阻点火(HVAR)	120-180sec @Thickness 3.00 mm	120-180sec @Thickness 0.118 in	UL 746A
Comparative Tracking Index跟踪指数	=600V @Thickness 3.00 mm	=600V @Thickness 0.118 in	IEC 60112
Hot Wire Ignition, HWI热线圈点燃测试	7.0-15sec @Thickness 1.50 mm	7.0-15sec @Thickness 0.0591 in	UL 746A
	15-30sec @Thickness 3.00 mm	15-30sec @Thickness 0.118 in	UL 746A
High Amp Arc Ignition, HAI高电流电弧点燃测试	=120arcs @Thickness 0.380 mm	=120arcs @Thickness 0.0150 in	UL 746A
High Voltage Arc-Tracking Rate, HVTR高压电弧跟踪速度	10.0-25.4mm/min @Thickness 3.00 mm	0.394-1.00in/min @Thickness 0.118 in	UL 746A
Thermal Properties热性能	Metric公制数据	English英制数据	Comments测试方法
CTE, linear线性热膨胀系数	11.0μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	6.11μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359
CTE, linear, Transverse to Flow线性热膨胀系数/横向	11.0μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	6.11μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359

ECO-315是美国首诺公司半晶体-晶体物质聚己二酸己二胺树脂即聚酰胺尼龙66型号之一,商品名Vydyne,是一种产量最大,品种最多,用途最广的塑胶原料,具有优良的机械强度,优良的韧性,优秀的力学性能,优秀的自润滑性,优秀的耐摩性,优秀的电绝缘性,良好的耐热性,良好的耐气候性,广泛用于机械领域、汽车领域、电子电器领域、纺织行业、化工行业、航空冶金等领域。

美国奥升德VYDYNE?PA66 ECO315是一种经过了阻燃添加剂的改进，以帮助用户满足保险商实验室对模塑件的易燃性等级要求。
与普通用途的无增强尼龙6,6相比，阻燃添加剂降低了韧性和延展性，而ECO315则是为了将这种延展性损失降到最低。该产品通常比其他(UL) 94V-0塑料材料在商业应用中具有更多的延展性。
Vydyne?ECO315是一种相对较低比重的阻燃树脂。有意义的模塑材料的经济比较必须基于每立方英寸的成本，这是通过降低比重来降低的。
ECO315的模收缩本质上相当于通用尼龙6,6树脂的模收缩，而尼龙6,6树脂通常用于许多电气/电子元件和其他需要(UL) 94V-2可燃性等级的部件。因此，现有的94V-2尼龙部件的模具通常可以用于从Vydyne?ECO315生产94V-0部件，消除了更换模具的延迟和成本。

PA66（聚酰胺66或尼龙66），同PA6相比，PA66*广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。