| MVR（300°C/1.2 kg）19 cm3/10分钟；通用；低粘度；易脱模；注塑成型-熔融温度280-320°C；可提供透明、半透明和不透明颜色 MVR (300 °C/1.2 kg) 19 cm3/10 min; general purpose; low viscosity; easy release; injection molding - melt temperature 280 - 320 °C; available in transparent, translucent and opaque colors |
产品描述Product Description
厂家：德国科思创Covestro - PUR
类别：PCPolycarbonate
用途：通用;
颜色：可用颜色,清晰/透明,半透明,不透明
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB; 含脱模剂; 防火阻燃等级V-2; 低粘度;Low Viscosity,Good stripping performance,HB,V-2
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density (73°F) | 1.20 | g/cm3 | ISO 1183 |
| 表观密度Apparent Density 22 | 0.66 | g/cm3 | ISO 60 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 300℃，1.20kg300℃/1.2 kg | 20 | g/10min | ISO 1133 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 300℃，1.2 kg300℃/1.2 kg | 19.0 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | |||
| TDAcross Flow | 0.50 to 0.70 | % | ISO 2577 |
| MDFlow | 0.50 to 0.70 | % | ISO 2577 |
| TD：2.0 mmAcross Flow : 0.0787 in 33 | 0.70 | % | ISO 294-4 |
| MD：2.0 mmFlow : 0.0787 in 33 | 0.65 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃饱和，23℃ | 0.30 | % | ISO 62 |
| 平衡，23℃，50% RH平衡，23℃，50% RH | 0.12 | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 水气透过率水气透过率 | |||
| 23℃，85% RH，100 μm23℃，85% RH，100 μm | 15 | g/m2/24 hr | ISO 15106-1 |
| 气体渗透Gas Permeation | ISO 2556 | ||
| 二氧化碳：23℃，25.4 μmCarbon Dioxide : 23°C, 25.4 μm | 18900 | cm3/m2/bar/24 hr | ISO 2556 |
| 二氧化碳：23℃，100.0 μmCarbon Dioxide : 23°C, 100.0 μm | 4000 | cm3/m2/bar/24 hr | ISO 2556 |
| 氮气：23℃，25.4 μmNitrogen : 23°C, 25.4 μm | 630 | cm3/m2/bar/24 hr | ISO 2556 |
| 氮气：23℃，100.0 μmNitrogen : 23°C, 100.0 μm | 130 | cm3/m2/bar/24 hr | ISO 2556 |
| 氧气：23℃，25.4 μmOxygen : 23°C, 25.4 μm | 3150 | cm3/m2/bar/24 hr | ISO 2556 |
| 氧气：23℃，100.0 μmOxygen : 23°C, 100.0 μm | 700 | cm3/m2/bar/24 hr | ISO 2556 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength 66 | ISO 7391 | ||
| -30℃，完全断裂-22°F, Complete Break | 14 | kJ/m2 | ISO 7391 |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60℃-60°C | No Break | ISO 179/1eU | |
| -30℃-30°C | No Break | ISO 179/1eU | |
| 23℃23°C | No Break | ISO 179/1eU | |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength 77 | ISO 7391 | ||
| -30℃，完全断裂-22°F, Complete Break | 15 | kJ/m2 | ISO 7391 |
| 23℃，局部断裂73°F, Partial Break | 65 | kJ/m2 | ISO 7391 |
| 多轴向仪器化冲击能量Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30℃-30°C | 65.0 | J | ISO 6603-2 |
| 23℃23°C | 55.0 | J | ISO 6603-2 |
| 多轴向仪器化冲击力峰值Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30℃-30°C | 6000 | N | ISO 6603-2 |
| 23℃23°C | 5100 | N | ISO 6603-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 124 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火0.45 MPa，未退火 | 137 | ℃ | ISO 75-2/B |
| 玻璃化转变温度Glass Transition Temperature 138 | 144 | ℃ | ISO 11357-2 |
| 维卡软化温度Vicat Softening Temperature | |||
| B50-- | 145 | ℃ | ISO 306 |
| B120-- | 146 | ℃ | ISO 306/B120 |
| 球压测试球压测试 | |||
| 136℃136℃ | Pass | IEC 60695-10-2 | |
| 线性热膨胀系数线性热膨胀系数 | |||
| TD：23~55℃TD：23 到 55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
| MD：23~55℃MD：23 到 55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
| 导热系数导热系数9 | |||
| 23℃23℃9 | 0.20 | W/m/K | ISO 8302 |
| 相对温度指数相对温度指数 | |||
| 电气性能，1.50 mm电气性能，1.5 mm | 125 | ℃ | UL 746 |
| 强度机械性能，1.50 mm强度机械性能，1.5 mm | 125 | ℃ | UL 746 |
| 冲击机械性能，1.50 mm冲击机械性能，1.5 mm | 115 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| 体积电阻率体积电阻率 | |||
| 23℃23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| 介电强度介电强度 | |||
| 23 ℃，1 mm23℃，1.00 mm | 34 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 23℃，100 Hz23°C, 100 Hz | 3.10 | IEC 60250 | |
| 23℃，1 MHz23°C, 1 MHz | 3.00 | IEC 60250 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 23℃，100 Hz23°C, 100 Hz | 5.0E-4 | IEC 60250 | |
| 23℃，1 MHz23°C, 1 MHz | 9.0E-3 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | IEC 60112 | ||
| 解决方案 ASolution A | 250 | V | IEC 60112 |
| 解决方案 BSolution B | 125 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 2.70 mm2.7 mm | HB | UL 94 | |
| 0.36 mm0.36 mm | V-2 | UL 94 | |
| 0.75 mm0.75 mm | V-2 | UL 94 | |
| 灼热丝可燃性指数Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.75 mm0.75 mm | 850 | ℃ | IEC 60695-2-12 |
| 1.5 mm1.5 mm | 875 | ℃ | IEC 60695-2-12 |
| 3.0 mm3.0 mm | 930 | ℃ | IEC 60695-2-12 |
| 灼热丝起燃温度Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.75 mm0.75 mm | 875 | ℃ | IEC 60695-2-13 |
| 1 mm1.0 mm | 875 | ℃ | IEC 60695-2-13 |
| 1.5 mm1.5 mm | 875 | ℃ | IEC 60695-2-13 |
| 3 mm3.0 mm | 875 | ℃ | IEC 60695-2-13 |
| 极限氧指数Oxygen Index 1010 | 27 | % | ISO 4589-2 |
| 小型燃烧器火焰的应用小型燃烧器火焰的应用 | |||
| Method K and F，2.00 mmMethod K and F，2.00 mm | K1, F1 | DIN 53438-1, -3 | |
| 燃烧速率燃烧速率 | |||
| USFMVSS， 1.00 mmUSFMVSS， 1.00 mm | passed | ISO 3795 | |
| Flash Ignition TemperatureFlash Ignition Temperature | 480 | ℃ | ASTM D1929 |
| 针焰测试Needle Flame Test | IEC 60695-11-5 | ||
| Method F：1.50 mmMethod F : 1.50 mm | 1.0 | min | IEC 60695-11-5 |
| Method F：2.00 mmMethod F : 2.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method F：3.00 mmMethod F : 3.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method K：1.50 mmMethod K : 1.50 mm | 0.1 | min | IEC 60695-11-5 |
| Method K：2.00 mmMethod K : 2.00 mm | 0.1 | min | IEC 60695-11-5 |
| Method K：3.00 mmMethod K : 3.00 mm | 0.2 | min | IEC 60695-11-5 |
| 自燃温度Self Ignition Temperature | 550 | ℃ | ASTM D1929 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 折射率Refractive Index 1111 | 1.585 | ISO 489 | |
| 透光率Transmittance | ISO 13468-2 | ||
| 1000 μm1000 μm | 89.0 | % | ISO 13468-2 |
| 2000 μm2000 μm | 89.0 | % | ISO 13468-2 |
| 3000 μm3000 μm | 88.0 | % | ISO 13468-2 |
| 4000 μm4000 μm | 87.0 | % | ISO 13468-2 |
| 雾度雾度 | |||
| 3000 μm3000 μm | 0.80 | % | ISO 14782 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 电解腐蚀电解腐蚀 | |||
| 23℃23℃ | A1 | IEC 60426 | |
| ISO ShortnameISO Shortname | ISO 7391-PC,MR,(,,)-18-9 | ||
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量拉伸模量 | |||
| 23℃23℃ | 2400 | MPa | ISO 527-1-2 |
| 拉伸强度拉伸强度 | |||
| 断裂，23℃断裂，23℃ | 65.0 | MPa | ISO 527-2/50 |
| 屈服，23℃屈服，23℃ | 65.0 | MPa | ISO 527-2/50 |
| 拉伸应变拉伸应变 | |||
| 断裂，23℃断裂，23℃ | 130 | % | ISO 527-2/50 |
| 屈服，23℃屈服，23℃ | 6.0 | % | ISO 527-2/50 |
| 标称拉伸断裂应变标称拉伸断裂应变 | |||
| 23℃23℃ | 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr) | 2200 | MPa | ISO 899-1 |
| 拉伸蠕变模量拉伸蠕变模量 | |||
| 1000 hr1000 hr | 1900 | MPa | ISO 899-1 |
| 弯曲模量弯曲模量4 | |||
| 23℃23℃4 | 2350 | MPa | ISO 178 |
| 弯曲强度Flexural Stress 44 | ISO 178 | ||
| 3.50% 应变，23℃3.5% Strain, 23°C | 73.0 | MPa | ISO 178 |
| 23℃23°C | 97.0 | MPa | ISO 178 |
| 弯曲应变Flexural Strain at Flexural Strength 5 (23°C)5 | 7.1 | % | ISO 178 |
| 球压硬度Ball Indentation Hardness | 115 | MPa | ISO 2039-1 |
联系方式
江苏普及塑料有限公司
联系人：
何志伟
服务热线：
딡륀삄딡삄ꂂ
딡륀삄딡삄ꂂ
公司地址：
陆家镇陆丰东路3号仕泰隆模具城M区511室
该企业其他产品
-
注塑级 PP利安德巴塞尔 HP525N 高清晰度 食品接触 易加工 高刚性￥0.01元
-
PP 韩国sk B391G 高抗冲共聚物 高流动 高刚性 食品级 40熔融指数￥0.01元
-
高流动PP 韩国sk/BX3920耐高温高抗冲高刚性注塑级￥0.01元
-
PP 韩国SK B380G 高流动 高抗冲 高光泽 用于家电部件 聚丙烯PP￥0.01元
-
PP韩国SK B330F尺寸稳定高抗撞抗冲共聚物高韧性电池盒电气/电子￥0.01元
-
注塑级 PP/韩国sk/B340F 高强度 高抗冲 共聚物 电子电器￥0.01元
-
PP台湾李长荣6331注塑颗粒低气味新料食品容器瓶盖均聚物塑胶原料￥0.01元
-
PP李长荣化工(福聚)PC366-3瓶盖料单聚合物高强度透明PP料PC366-4￥0.01元
科思创PC 2405 高流动PC 照明灯具 汽车部件相关产品
- 厂家批发 蓝色6mm中空透明板 PC阳光板 温室大棚PC板
- PC 上海科思创（拜耳） 2407塑胶原料PC 塑料
- PC塑胶原料 PC 上海科思创（拜耳） 2405价格
- 塑胶原料PC 上海科思创（拜耳） 2405
- V-2阻燃级塑胶原料PC 上海科思创（拜耳） 2407
- PC上海科思创（拜耳） 2456高流动塑胶原料PC
- 通用塑料原料PC 上海科思创（拜耳） 2458
- 注塑级PC塑料原料上海科思创（拜耳） 2605
- 脱模性塑料原料PC上海科思创（拜耳） 2665
- PC塑料原料上海科思创（拜耳）2805通用级注塑级中粘度
- PC塑胶原料 沙比克/sabicDX11354白色LDS塑料
- 抗紫外线PC塑料原料上海科思创（拜耳） 2807
- 挤出级PC塑料原料上海科思创（拜耳） 2856
- 塑料原料价格PC 上海科思创（拜耳） 2865
- V-2阻燃级塑胶原料PC 上海科思创（拜耳） 3103
- PC沙比克塑胶原料DX11355黑色LDS天线专用塑料
- PC塑胶原料批发上海科思创（拜耳） 3105
- PC塑胶原料厂家上海科思创（拜耳） 3206
猜你在找
- PC 沙伯基础 144R-111FC 食品级
- PC 日本出光 IRY2200 阻燃 中粘度 抗UV 电池盒 打印机电器外壳应用
- PC 日本出光 LC1500 高流动 高抗冲 应用液晶导光板
- 生产中专用料充电器外壳高光白色ABS改性厂家省钱原料
- 自产自销PC PC/ABS 白度88-99 可根据产品订制现有颜色色号20+新料改性塑造料
- 销售黑色PC 基础创新塑料 南沙 DX11355-BKNATPC 塑胶原料价格 PC塑料颗粒
- 原厂原包白色PC 基础创新塑料 南沙 DX11354X塑胶原料 PC工程塑料价格
- 专卖黑色工程塑料PC 基础创新塑料 南沙 141R-701塑胶原料价格 PC高流动塑胶原料
- 销售PC 基础创新塑料 上海 141R-111工程塑料PC塑料价格
- 耐冲击PC塑料价格/上海科思创 拜耳 2605 适用于电子电器制品
- PC原料价格/上海科思创 拜耳 2458 耐高温PC塑胶
- 专注高抗冲PC原料/上海科思创 拜耳 2456 高耐冲击塑胶原料
免责声明：以上展示的科思创PC 2405 高流动PC 照明灯具 汽车部件信息由江苏普及塑料有限公司自行提供，内容的真实性、准确性和合法性由发布企业负责，
全球塑胶网对此不承担责任。
风险防范建议：为保障您的利益，建议优先选择速购通会员
手机版：科思创PC 2405 高流动PC 照明灯具 汽车部件
更新产品链接为：https://www.51pla.com/html/sellinfo/485/48535837.htm
公司名片
发送询价单