SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PAPolyphenylene Ether/PPO

SABIC Innovative Plastics (GE Plastics)

产品说明：

Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.26 g/cc	1.26 g/cc	ASTM D792
密度	1.26 g/cc	0.0455 lb/in3	ISO 1183
水分吸收	0.500 %	0.500 %	23°C / 50% RH; ISO 62
饱和吸水率	4.0 %	4.0 %	ISO 62
线性成型收缩率,Flow	0.0026 - 0.0030 cm/cm @Thickness 3.20 mm	0.0026 - 0.0030 in/in @Thickness 0.126 in	SABIC Method
线性成型收缩率，横向	0.0072 - 0.0085 cm/cm @Thickness 3.20 mm	0.0072 - 0.0085 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	8.6 g/10 min @Load 5.00 kg, Temperature 280 °C	8.6 g/10 min @Load 11.0 lb, Temperature 536 °F	ASTM D1238
化合物熔体指数	7.0 g/10 min @Load 5.00 kg, Temperature 280 °C	7.0 g/10 min @Load 11.0 lb, Temperature 536 °F	MVR [cm^3/10 min]; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	140 MPa	20300 psi	Type I, 5 mm/min; ASTM D638
	140 MPa	20300 psi	5 mm/min; ISO 527
抗张强度(屈服)	140 MPa	20300 psi	Type I, 5 mm/min; ASTM D638
	140 MPa	20300 psi	5 mm/min; ISO 527
伸长率 (断裂)	4.0 %	4.0 %	Type I, 5 mm/min; ASTM D638
	4.0 %	4.0 %	5 mm/min; ISO 527
屈服伸长率	3.1 %	3.1 %	Type I, 5 mm/min; ASTM D638
	3.1 %	3.1 %	5 mm/min; ISO 527
拉伸模量	7.00 GPa	1020 ksi	5 mm/min; ASTM D638
	7.00 GPa	1020 ksi	1 mm/min; ISO 527
弯曲强度	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D790
	200 MPa	29000 psi	2 mm/min; ISO 178
弯曲模量	6.60 GPa	957 ksi	1.3 mm/min, 50 mm span; ASTM D790
	6.60 GPa	957 ksi	2 mm/min; ISO 178
悬壁梁缺口冲击强度	0.850 J/cm	1.59 ft-lb/in	ASTM D256
	0.600 J/cm @Temperature -30.0 °C	1.12 ft-lb/in @Temperature -22.0 °F	ASTM D256
	10.0 kJ/m2	4.76 ft-lb/in2	80*10*4; ISO 180/1A
	8.00 kJ/m2 @Temperature -30.0 °C	3.81 ft-lb/in2 @Temperature -22.0 °F	80*10*4; ISO 180/1A
简支梁缺口冲击强度	1.10 J/cm2	5.23 ft-lb/in2	Edgew 80*10*4 sp=62mm; ISO 179/1eA
落锤总能量	17.0 J @Temperature 23.0 °C	12.5 ft-lb @Temperature 73.4 °F	ASTM D3763

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	1000 - 10000 ohm-cm	1000 - 10000 ohm-cm	SABIC Method

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	23.0 μm/m-°C @Temperature -40.0 - 40.0 °C	12.8 μin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	23.0 μm/m-°C @Temperature -40.0 - 40.0 °C	12.8 μin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
线性热膨胀系数,横向流动	80.0 μm/m-°C @Temperature -40.0 - 40.0 °C	44.4 μin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	80.0 μm/m-°C @Temperature -40.0 - 40.0 °C	44.4 μin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
载荷下热变形温度(0.46 MPa)	215 °C	419 °F	Flatw 80*10*4 sp=64mm; ISO 75/Bf
	215 °C @Thickness 3.20 mm	419 °F @Thickness 0.126 in	unannealed; ASTM D648
维卡软化温度	215 °C	419 °F	Rate B/50; ASTM D1525
	215 °C	419 °F	Rate B/50; ISO 306
	225 °C	437 °F	Rate B/120; ISO 306