InnoPlus LL7410ALinear Low Density Polyethylene

PTT Global Chemical Public Company Limited

产品说明：

InnoPlus LL7410A resin is a linear low density polyethylene with butene comonomers, without slip and antiblock. This grade offers the excellent machinability on conversion lines. Film extruded from InnoPlus LL7410A have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing. Besides, this grade can be used for blending with HDPE as well.

InnoPlus LL7410A is recommended for producing the general purpose films, liners, heavy duty films, food packaging and agricultural films.

物性信息：

基本信息
特性	丁烯共聚单体 高拉伸强度 抗穿孔性 可切削 韧性良好 无添加剂 延高的拉伸率
用途	薄膜 衬里 混合 农业应用 食品包装
形式	粒子
加工方法	薄膜挤出 吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.918	g/cm3	ASTM D792
熔流率（熔体流动速率）(190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 D, 模压成型)	52		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 模压成型	11.0	MPa	ASTM D638
断裂, 模压成型	28.0	MPa	ASTM D638
伸长率(断裂, 模压成型)	790	%	ASTM D638
弯曲模量(模压成型)	310	MPa	ASTM D790

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	25	μm
割线模量			ASTM D882
1% 正割, MD : 25 μm, 吹塑薄膜	190	MPa	ASTM D882
1% 正割, TD : 25 μm, 吹塑薄膜	220	MPa	ASTM D882
抗张强度			ASTM D882
MD : 断裂, 25 μm, 吹塑薄膜	34.0	MPa	ASTM D882
TD : 断裂, 25 μm, 吹塑薄膜	26.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 25 μm, 吹塑薄膜	700	%	ASTM D882
TD : 断裂, 25 μm, 吹塑薄膜	900	%	ASTM D882
落锤冲击(25 μm, 吹塑薄膜)	100	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 25 μm, 吹塑薄膜	100	g	ASTM D1922
TD : 25 μm, 吹塑薄膜	350	g	ASTM D1922

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度(模压成型)	440	J/m	ASTM D256

热性能	额定值	单位制	测试方法
维卡软化温度	96.0	°C	ASTM D1525
熔融峰值温度	121	°C	ASTM D3418

光学性能	额定值	单位制	测试方法
光泽度(45°, 25.0 μm, 吹塑薄膜)	55		ASTM D2457
雾度(25.0 μm, 吹塑薄膜)	10	%	ASTM D1003

挤出	额定值	单位制
熔体温度	160 到 180	°C
口模温度	170 到 190	°C